Steel Pipe Crack Analysis

I believe that every manufacturer wants to produce high quality products, on the one hand to reduce input costs, on the other hand to save time. But in the actual production process often occur some of the details to cause steel tube surface cracks, Why?

First, the production material of alloy steel pipe is uneven, in the production process, inferior raw materials can not withstand high temperature or high pressure to cause the organization fracture, naturally produced the steel pipe quality is not up to standard.

Secondly, the cooling process be rushed, when the steel pipe production is completed, usually involving a cooling process, if this time too hasty, the cooling process will be cracks.

Therefore, in the process of producing alloy steel tube, be sure to forging steel pipe time and temperature control operations must be reasonable, thus produced steel pipe will be qualified.